Coated 8011 8006 Hydrophilic Aluminium Foil / Aluminum Fin for Air Conditioner 8011 8006 manufacturer from China ZHEJIANG SHUANGLIN JIATE METAL TECHNOLOGY CO., LTD.

Coated 8011 8006 Hydrophilic Aluminium Foil / Aluminum Fin for Air Conditioner

Place of Origin:

Zhejiang, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Model No.: 8011 8006

High Quality 8011 8006 Hydrophilic Aluminium Foil / Aluminum Fin for Air Conditioner

Aluminium fi

High Quality 8011 8006 Hydrophilic Aluminium Foil / Aluminum Fin for Air Conditioner

Aluminium fin foil :
hydrophilic aluminium foil finstock is widely used in household air conditioner ,refrigerrator ,cold equipment and vehicle air ec
1. alloy :1100,1200,1145,8011,8006
2. temper :h12,h14,h16,h18 ,h22,O
3. thicknes:0.08mm to 0.25mm
4. widht :20mm to 2100mm

our company ajust the alloy and develop DS-1,DS-2,DS-3 which are good in mechanical and hydrophilic capability on the basis of 1100,1200,1145,8006 with all kinds of size !

Place of Origin	Zhejiang, China (Mainland)
Brand Name	Jinding
Model Number	1060
Grade	1000 Series
Thickness	0.08mm --0.25mmm
Width	80mm --1240mm
Application	hydrophilic aluminium finstock
Surface Treatment	Coated
Hardness	30
Alloy Or Not	Non-alloy
Al (Min)	99.5
Yield (≥ MPa)	7o
Temper	O - H112
Ultimate Strength (≥ MPa)	100
Elongation (≥ %)	10

Product Brief Introduction:

() Aluminum Coil/Foil Used for Air Conditioner and Others (packing.Cable and pipe)

Alloy ,temper,Physical Properties under Room Temperature

Alloy	Temper	Physical Properties under Room Temperature
Alloy	Temper	U.T.S 6 b ,Mpa	Elongation e%	Cupping Value IE,mm
1100 1200 1235 8079 8011	O	80110	≥20	≥6.0
	H22	100135	≥16	≥5.5
	H24	115145	≥12	≥5.0
	H26	125160	≥8	≥4.0
	H18	≥160	≥1	--
Mark: Special specifications you need can be negotiated and marked in the contract

Thickness & Tolerance mm	Width & Tolerance mm	Core I. D. mm	Max. Roll O. D. mm	Core Material
0.0090.02	1001100 ±0.5	Φ75,Φ150,Φ200	Φ≤1400	Paper, Aluminum, Steel

The Coat Properties of Hydrophilic Coated Foil:

No.	Item Index		Technology Index
1	Film Thickness		1.0-2.0μm(Average Thickness for Single Face)
2	Hydrophilicity	Initial Contact Angle	Initial Contact Angle≤10°
		Persistent Contact Angle	Persistent Contact Angle≤20°
3	Adhesive Power		Cupping Testing(5mm pressed by): no Flake Girding Testing(100/100): No Delaminating
4	Corrosion Resistance		Salt Spray Testing(72 hours) R.N≥9.50
5	Alkali Resistance		Soaked in 20,20%NaOH for 3 minutes The sample coat will completely not bubble
6	Solvent Resistance		Weight Loss of Sample≤1%
7	Stability		under 200 for 5 min, the color will not change under 300 for 5 min, coat will be light yellow
8	Oil Resistance		Soaked in volatile oil for 24 hours without bubbling
9	Coat Odor		No Peculiar Odor
10	Abrasion against Mould		The Same as Common Aluminum Foil